Failure of a 17-4 PH stainless steel sailboat propeller shaft

In this study, a 17-4 PH precipitation hardening stainless steel propeller shaft failed in use when installed in a sailboat working in a marine environment. Failure analysis was conducted on the propeller shaft. Results indicate that the failure was caused by the fracture of the propeller shaft by t...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Engineering failure analysis 2003-12, Vol.10 (6), p.711-717
Hauptverfasser:	Arisoy, C.Fahir, Başman, Gokhan, Şeşen, M.Kelami
Format:	Artikel
Sprache:	eng
Schlagworte:	Failure analysis Fatigue Martensite Shafts Stress corrosion cracking