Influence of paper mixing pads thickness on the compressive strength of glass ionomer cement

To explore the influence of the thickness of mixed cardboard on the compressive strength of glass ionomer cement and the associated factors. Three different types of glass ionomer cements were mixed on the top of 60, 40, 20 and 1 pieces of paper (P60, P40, P20 and P1), respectively. The compressive strength of the materials was tested after solidification, and the bubble rate was calculated with the assistance of scanning electron microscope. (1) Compressive strength: ① ChemFil Superior glass ionomer (CF): The average compressive strength of P1 group was the highest, which was significantly different from that of P40 and P60 groups ( values were 0.041 and 0.032 respectively); ② To Fuji IX GP glass ionomer (IX): The average compressive strength of P1 group was the highest, which was statistically different from that of P40 and P60 groups ( values were 0.042 and 0.038 respectively); ③ Glaslonomer FX-Ⅱ glass ionomer cement (FX): The average compressive strength of P1 group was the highest, which was statisticall