Influence of foreign-object damage on crack initiation and early crack growth during high-cycle fatigue of Ti–6Al–4V

The objective of this work is to provide a rationale approach to define the limiting conditions for high-cycle fatigue (HCF) in the presence of foreign-object damage (FOD). This study focused on the role of simulated FOD in affecting the initiation and early growth of small surface fatigue cracks in...