Modes of dynamic shear failure in solids

The technique of loading edge cracks by edge impact (LECEI) for generating high rates of crack tip shear (mode-II) loading is presented. The LECEI-technique in combination with a gas gun for accelerating the impactor is used to study the high rate shear failure behaviour of three types of materials....

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of fracture 2000-01, Vol.101 (1-2), p.1-31
1. Verfasser:	Kalthoff, Joerg F
Format:	Artikel
Sprache:	eng
Schlagworte:	Adiabatic flow Aluminum base alloys Compressive properties Control stability Crack initiation Crack propagation Crack tips Cracks Edge cracks Edge dislocations Energy Epoxy resins Equivalence Failure modes Flux density Gas guns Loading rate Maraging steels Plastic zones Shear bands Stress concentration Stress distribution Stress propagation