Strain induced directional coarsening in nickel based superalloys: Investigation on kinetics using the small angle neutron scattering (SANS) technique

Using the small angle neutron scattering technique, we have observed rafting in nickel based single crystal superalloys. Kinetics of morphological evolution of the precipitates have been studied in situ. Therefore we used a special furnace designed for the ageing of prestrained specimens under a neutron beam. The evolution of both the precipitate aspect ratio and the distance between precipitates confirms the importance of strain in the directional coarsening process. Results are presented and discussed regarding kinetics and microstructural aspects. In such conditions, rafts seem to be different from those obtained after a creep test. Nous avons observé la coalescence orientée dans les superalliages monocristallins à base de nickel en utilisant la technique de diffusion aux petits angles des neutrons. La cinétique de l'évolution morphologique des précipités a été étudiée “in situ”. Pour cela, nous avons utilisé un four développé spécialement, pour effectuer des traitements de vieillissement, sous le faisceau, d'un échantillon prédéformé. L'évolution des facteurs de forme des précipités et de la distance moyenne entre ces précipités confirme l'importance de la prédéformation dans le processus de coalescence orientée. La présentation et la discussion des résultats concernent à la fois les aspects cinétiques et microstructuraux. Les radeaux obtenus dans ces conditions semblent différents de ceux résultant d'un essai de fluage.