Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels

Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Engineering failure analysis 2002-04, Vol.9 (2), p.167-184
Hauptverfasser:	Eliaz, N., Shachar, A., Tal, B., Eliezer, D.
Format:	Artikel
Sprache:	eng
Schlagworte:	Failure analysis Hydrogen embrittlement Stress-corrosion cracking Structural steel Tempered martensite embrittlement