Oxidation behaviour of NiAl—II. Cavity formation beneath the oxide scale on NiAl of different stoichiometries

The formation of voids at the metal/oxide interface was observed after the oxidation of NiAl in the temperature range 1173–1473 K. The number of voids and extent of the undermining of the scale increased with the Ni content of the NiAl. The growth of the voids to large cavities led to loss of scale...