Effects of shade and thickness on the translucency parameter of anatomic-contour zirconia, transmitted light intensity, and degree of conversion of the resin cement
Anatomic-contour zirconia prostheses are usually cemented with resin cement. However, information regarding the effects of the zirconia shade and thicknesses on the translucency of the prosthesis, the intensity of the transmitted light beneath the prosthesis, and the subsequent degree of conversion...
Gespeichert in:
| Veröffentlicht in: | The Journal of prosthetic dentistry 2023-01, Vol.129 (1), p.213-219 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | eng |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| container_end_page | 219 |
|---|---|
| container_issue | 1 |
| container_start_page | 213 |
| container_title | The Journal of prosthetic dentistry |
| container_volume | 129 |
| creator | Supornpun, Noppamath Oster, Molly Phasuk, Kamolphob Chu, Tien-Min G. |
| description | Anatomic-contour zirconia prostheses are usually cemented with resin cement. However, information regarding the effects of the zirconia shade and thicknesses on the translucency of the prosthesis, the intensity of the transmitted light beneath the prosthesis, and the subsequent degree of conversion in the resin cement is sparse.
The purpose of this in vitro study was to investigate the translucency parameter in 3 anatomic-contour zirconia specimens of 2 shades at 5 different thicknesses and to investigate the transmitted light intensity and degree of conversion of the resin cement beneath the ceramic specimens by using a traditional zirconia and a lithium disilicate glass-ceramic as controls.
Ceramic specimens from 1 anatomic-contour zirconia in a generic shade (CAP FZ) and 2 anatomic-contour zirconias in A2 shade (Zirlux and Luxisse) were used. Lithium disilicate in HT A2 shade (IPS e.max CAD) and traditional zirconia in a generic shade (CAP QZ) were used as controls. A total of 125 ceramic specimens (n=25) were fabricated to a final specimen dimension of 12×12 mm and in thicknesses of 1.0, 1.25, 1.5, 1.75, and 2.0 mm according to the manufacturers’ recommendations. The CIELab color space for all specimens placed against a white and black background was measured with a spectrophotometer (CM-2600D), and the translucency parameters were calculated for the materials at various thicknesses. A light-polymerizing unit (DEMI LED) was used to polymerize the resin cement (Variolink II) placed beneath the ceramic specimens. Transmitted light intensity from the polymerization unit beneath the ceramic specimens was measured by using a spectrophotometer (MARC Resin Calibrator), and the transmittance of each specimen was calculated. The coefficient of absorption of each material was calculated from the regression analysis between the natural log of transmittance and specimen thickness. The degree of conversion of resin cement was measured by using a Fourier transformation infrared (FTIR) spectrophotometer. The results were analyzed by using 2-way ANOVA (α=.05). The relationship between the transmittance and the translucency parameter was evaluated by plotting the transmittance against the translucency parameter value of each specimen.
The translucency parameter decreased with increasing thickness in all 5 material groups. All anatomic-contour zirconia had lower translucency parameters than e.max CAD (P |
| doi_str_mv | 10.1016/j.prosdent.2021.04.019 |
| format | Article |
| fullrecord | <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_miscellaneous_2540514386</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><els_id>S0022391321002511</els_id><sourcerecordid>2540514386</sourcerecordid><originalsourceid>FETCH-LOGICAL-c482t-cd72cb032dab19a6261fe87769060813fb5cf7e73b2726f5fea4a92fc003f24d3</originalsourceid><addsrcrecordid>eNqFkc9u1DAQxi0EokvhFSofOTRhbCdOcgNV5Y9UiQucLcced70kzmI7lZbn4UFx2JYrJ3tG3zefZn6EXDGoGTD57lAf45Ishlxz4KyGpgY2PCM7BkNXyb5hz8kOgPNKDExckFcpHQCgbzv2klyIhjHZi35Hft86hyYnujia9toi1cHSvPfmR8BU2qEUSHPUIU2rwWBO9KijnjFj3Ew66LzM3lRmCXlZI_3lY_l6fX02zT5ntHTy9_tMfcgYks-n678xFu8j4jalOB4wJl_iSrUlRkw-UINzWfE1eeH0lPDN43tJvn-8_Xbzubr7-unLzYe7yjQ9z5WxHTcjCG71yAYtuWQO-66TA0jomXBja1yHnRh5x6VrHepGD9wZAOF4Y8UleXueW277c8WU1eyTwWnSAZc1Kd420LJG9LJI5VlqCoYU0alj9LOOJ8VAbYTUQT0RUhshBY0qhIrx6jFjHWe0_2xPSIrg_VmAZdMHj1El48vd0fpYSCm7-P9l_AHP36oB</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>2540514386</pqid></control><display><type>article</type><title>Effects of shade and thickness on the translucency parameter of anatomic-contour zirconia, transmitted light intensity, and degree of conversion of the resin cement</title><source>MEDLINE</source><source>Elsevier ScienceDirect Journals</source><creator>Supornpun, Noppamath ; Oster, Molly ; Phasuk, Kamolphob ; Chu, Tien-Min G.</creator><creatorcontrib>Supornpun, Noppamath ; Oster, Molly ; Phasuk, Kamolphob ; Chu, Tien-Min G.</creatorcontrib><description>Anatomic-contour zirconia prostheses are usually cemented with resin cement. However, information regarding the effects of the zirconia shade and thicknesses on the translucency of the prosthesis, the intensity of the transmitted light beneath the prosthesis, and the subsequent degree of conversion in the resin cement is sparse.
The purpose of this in vitro study was to investigate the translucency parameter in 3 anatomic-contour zirconia specimens of 2 shades at 5 different thicknesses and to investigate the transmitted light intensity and degree of conversion of the resin cement beneath the ceramic specimens by using a traditional zirconia and a lithium disilicate glass-ceramic as controls.
Ceramic specimens from 1 anatomic-contour zirconia in a generic shade (CAP FZ) and 2 anatomic-contour zirconias in A2 shade (Zirlux and Luxisse) were used. Lithium disilicate in HT A2 shade (IPS e.max CAD) and traditional zirconia in a generic shade (CAP QZ) were used as controls. A total of 125 ceramic specimens (n=25) were fabricated to a final specimen dimension of 12×12 mm and in thicknesses of 1.0, 1.25, 1.5, 1.75, and 2.0 mm according to the manufacturers’ recommendations. The CIELab color space for all specimens placed against a white and black background was measured with a spectrophotometer (CM-2600D), and the translucency parameters were calculated for the materials at various thicknesses. A light-polymerizing unit (DEMI LED) was used to polymerize the resin cement (Variolink II) placed beneath the ceramic specimens. Transmitted light intensity from the polymerization unit beneath the ceramic specimens was measured by using a spectrophotometer (MARC Resin Calibrator), and the transmittance of each specimen was calculated. The coefficient of absorption of each material was calculated from the regression analysis between the natural log of transmittance and specimen thickness. The degree of conversion of resin cement was measured by using a Fourier transformation infrared (FTIR) spectrophotometer. The results were analyzed by using 2-way ANOVA (α=.05). The relationship between the transmittance and the translucency parameter was evaluated by plotting the transmittance against the translucency parameter value of each specimen.
The translucency parameter decreased with increasing thickness in all 5 material groups. All anatomic-contour zirconia had lower translucency parameters than e.max CAD (P<.001). The same results were found for the intensity of the transmitted light (P<.001). Both A2 shade anatomic-contour zirconia (Zirlux and Luxisse) showed significantly lower light transmittance than a generic shade anatomic-contour zirconia (CAP FZ) (P<.001). The coefficients of absorption were found to range from 0.63 to 1.72 mm-1, and reflectance from 0.10 to 0.25. The results from the degree of conversion of resin cement after polymerization through 1 to 2 mm of specimens showed a significantly higher degree of conversion in the e.max group than in all other groups (P<.001). The correlation between translucency parameter and the intensity of the transmitted light suggested that the relationship was shade dependent.
The translucency parameter and the transmitted light intensity of ceramic material were influenced by the type of ceramic and the shade and thickness of the ceramic. The combined effects of layer thickness and the intensity of the transmitted light in the A2 shade anatomic-contour zirconia (Zirlux and Luxisse) resulted in a lower degree of conversion in resin cement than in a generic shade anatomic-contour zirconia (CAP FZ) at layer thicknesses of 1.75 and 2 mm.</description><identifier>ISSN: 0022-3913</identifier><identifier>EISSN: 1097-6841</identifier><identifier>DOI: 10.1016/j.prosdent.2021.04.019</identifier><identifier>PMID: 34116838</identifier><language>eng</language><publisher>United States: Elsevier Inc</publisher><subject>Ceramics - therapeutic use ; Color ; Dental Porcelain ; Light ; Materials Testing ; Resin Cements - therapeutic use ; Surface Properties</subject><ispartof>The Journal of prosthetic dentistry, 2023-01, Vol.129 (1), p.213-219</ispartof><rights>2021 Editorial Council for the Journal of Prosthetic Dentistry</rights><rights>Copyright © 2021 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.</rights><lds50>peer_reviewed</lds50><oa>free_for_read</oa><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c482t-cd72cb032dab19a6261fe87769060813fb5cf7e73b2726f5fea4a92fc003f24d3</citedby><cites>FETCH-LOGICAL-c482t-cd72cb032dab19a6261fe87769060813fb5cf7e73b2726f5fea4a92fc003f24d3</cites></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktohtml>$$Uhttps://www.sciencedirect.com/science/article/pii/S0022391321002511$$EHTML$$P50$$Gelsevier$$H</linktohtml><link.rule.ids>314,776,780,3537,27903,27904,65309</link.rule.ids><backlink>$$Uhttps://www.ncbi.nlm.nih.gov/pubmed/34116838$$D View this record in MEDLINE/PubMed$$Hfree_for_read</backlink></links><search><creatorcontrib>Supornpun, Noppamath</creatorcontrib><creatorcontrib>Oster, Molly</creatorcontrib><creatorcontrib>Phasuk, Kamolphob</creatorcontrib><creatorcontrib>Chu, Tien-Min G.</creatorcontrib><title>Effects of shade and thickness on the translucency parameter of anatomic-contour zirconia, transmitted light intensity, and degree of conversion of the resin cement</title><title>The Journal of prosthetic dentistry</title><addtitle>J Prosthet Dent</addtitle><description>Anatomic-contour zirconia prostheses are usually cemented with resin cement. However, information regarding the effects of the zirconia shade and thicknesses on the translucency of the prosthesis, the intensity of the transmitted light beneath the prosthesis, and the subsequent degree of conversion in the resin cement is sparse.
The purpose of this in vitro study was to investigate the translucency parameter in 3 anatomic-contour zirconia specimens of 2 shades at 5 different thicknesses and to investigate the transmitted light intensity and degree of conversion of the resin cement beneath the ceramic specimens by using a traditional zirconia and a lithium disilicate glass-ceramic as controls.
Ceramic specimens from 1 anatomic-contour zirconia in a generic shade (CAP FZ) and 2 anatomic-contour zirconias in A2 shade (Zirlux and Luxisse) were used. Lithium disilicate in HT A2 shade (IPS e.max CAD) and traditional zirconia in a generic shade (CAP QZ) were used as controls. A total of 125 ceramic specimens (n=25) were fabricated to a final specimen dimension of 12×12 mm and in thicknesses of 1.0, 1.25, 1.5, 1.75, and 2.0 mm according to the manufacturers’ recommendations. The CIELab color space for all specimens placed against a white and black background was measured with a spectrophotometer (CM-2600D), and the translucency parameters were calculated for the materials at various thicknesses. A light-polymerizing unit (DEMI LED) was used to polymerize the resin cement (Variolink II) placed beneath the ceramic specimens. Transmitted light intensity from the polymerization unit beneath the ceramic specimens was measured by using a spectrophotometer (MARC Resin Calibrator), and the transmittance of each specimen was calculated. The coefficient of absorption of each material was calculated from the regression analysis between the natural log of transmittance and specimen thickness. The degree of conversion of resin cement was measured by using a Fourier transformation infrared (FTIR) spectrophotometer. The results were analyzed by using 2-way ANOVA (α=.05). The relationship between the transmittance and the translucency parameter was evaluated by plotting the transmittance against the translucency parameter value of each specimen.
The translucency parameter decreased with increasing thickness in all 5 material groups. All anatomic-contour zirconia had lower translucency parameters than e.max CAD (P<.001). The same results were found for the intensity of the transmitted light (P<.001). Both A2 shade anatomic-contour zirconia (Zirlux and Luxisse) showed significantly lower light transmittance than a generic shade anatomic-contour zirconia (CAP FZ) (P<.001). The coefficients of absorption were found to range from 0.63 to 1.72 mm-1, and reflectance from 0.10 to 0.25. The results from the degree of conversion of resin cement after polymerization through 1 to 2 mm of specimens showed a significantly higher degree of conversion in the e.max group than in all other groups (P<.001). The correlation between translucency parameter and the intensity of the transmitted light suggested that the relationship was shade dependent.
The translucency parameter and the transmitted light intensity of ceramic material were influenced by the type of ceramic and the shade and thickness of the ceramic. The combined effects of layer thickness and the intensity of the transmitted light in the A2 shade anatomic-contour zirconia (Zirlux and Luxisse) resulted in a lower degree of conversion in resin cement than in a generic shade anatomic-contour zirconia (CAP FZ) at layer thicknesses of 1.75 and 2 mm.</description><subject>Ceramics - therapeutic use</subject><subject>Color</subject><subject>Dental Porcelain</subject><subject>Light</subject><subject>Materials Testing</subject><subject>Resin Cements - therapeutic use</subject><subject>Surface Properties</subject><issn>0022-3913</issn><issn>1097-6841</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2023</creationdate><recordtype>article</recordtype><sourceid>EIF</sourceid><recordid>eNqFkc9u1DAQxi0EokvhFSofOTRhbCdOcgNV5Y9UiQucLcced70kzmI7lZbn4UFx2JYrJ3tG3zefZn6EXDGoGTD57lAf45Ishlxz4KyGpgY2PCM7BkNXyb5hz8kOgPNKDExckFcpHQCgbzv2klyIhjHZi35Hft86hyYnujia9toi1cHSvPfmR8BU2qEUSHPUIU2rwWBO9KijnjFj3Ew66LzM3lRmCXlZI_3lY_l6fX02zT5ntHTy9_tMfcgYks-n678xFu8j4jalOB4wJl_iSrUlRkw-UINzWfE1eeH0lPDN43tJvn-8_Xbzubr7-unLzYe7yjQ9z5WxHTcjCG71yAYtuWQO-66TA0jomXBja1yHnRh5x6VrHepGD9wZAOF4Y8UleXueW277c8WU1eyTwWnSAZc1Kd420LJG9LJI5VlqCoYU0alj9LOOJ8VAbYTUQT0RUhshBY0qhIrx6jFjHWe0_2xPSIrg_VmAZdMHj1El48vd0fpYSCm7-P9l_AHP36oB</recordid><startdate>202301</startdate><enddate>202301</enddate><creator>Supornpun, Noppamath</creator><creator>Oster, Molly</creator><creator>Phasuk, Kamolphob</creator><creator>Chu, Tien-Min G.</creator><general>Elsevier Inc</general><scope>CGR</scope><scope>CUY</scope><scope>CVF</scope><scope>ECM</scope><scope>EIF</scope><scope>NPM</scope><scope>AAYXX</scope><scope>CITATION</scope><scope>7X8</scope></search><sort><creationdate>202301</creationdate><title>Effects of shade and thickness on the translucency parameter of anatomic-contour zirconia, transmitted light intensity, and degree of conversion of the resin cement</title><author>Supornpun, Noppamath ; Oster, Molly ; Phasuk, Kamolphob ; Chu, Tien-Min G.</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c482t-cd72cb032dab19a6261fe87769060813fb5cf7e73b2726f5fea4a92fc003f24d3</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng</language><creationdate>2023</creationdate><topic>Ceramics - therapeutic use</topic><topic>Color</topic><topic>Dental Porcelain</topic><topic>Light</topic><topic>Materials Testing</topic><topic>Resin Cements - therapeutic use</topic><topic>Surface Properties</topic><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>Supornpun, Noppamath</creatorcontrib><creatorcontrib>Oster, Molly</creatorcontrib><creatorcontrib>Phasuk, Kamolphob</creatorcontrib><creatorcontrib>Chu, Tien-Min G.</creatorcontrib><collection>Medline</collection><collection>MEDLINE</collection><collection>MEDLINE (Ovid)</collection><collection>MEDLINE</collection><collection>MEDLINE</collection><collection>PubMed</collection><collection>CrossRef</collection><collection>MEDLINE - Academic</collection><jtitle>The Journal of prosthetic dentistry</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Supornpun, Noppamath</au><au>Oster, Molly</au><au>Phasuk, Kamolphob</au><au>Chu, Tien-Min G.</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Effects of shade and thickness on the translucency parameter of anatomic-contour zirconia, transmitted light intensity, and degree of conversion of the resin cement</atitle><jtitle>The Journal of prosthetic dentistry</jtitle><addtitle>J Prosthet Dent</addtitle><date>2023-01</date><risdate>2023</risdate><volume>129</volume><issue>1</issue><spage>213</spage><epage>219</epage><pages>213-219</pages><issn>0022-3913</issn><eissn>1097-6841</eissn><abstract>Anatomic-contour zirconia prostheses are usually cemented with resin cement. However, information regarding the effects of the zirconia shade and thicknesses on the translucency of the prosthesis, the intensity of the transmitted light beneath the prosthesis, and the subsequent degree of conversion in the resin cement is sparse.
The purpose of this in vitro study was to investigate the translucency parameter in 3 anatomic-contour zirconia specimens of 2 shades at 5 different thicknesses and to investigate the transmitted light intensity and degree of conversion of the resin cement beneath the ceramic specimens by using a traditional zirconia and a lithium disilicate glass-ceramic as controls.
Ceramic specimens from 1 anatomic-contour zirconia in a generic shade (CAP FZ) and 2 anatomic-contour zirconias in A2 shade (Zirlux and Luxisse) were used. Lithium disilicate in HT A2 shade (IPS e.max CAD) and traditional zirconia in a generic shade (CAP QZ) were used as controls. A total of 125 ceramic specimens (n=25) were fabricated to a final specimen dimension of 12×12 mm and in thicknesses of 1.0, 1.25, 1.5, 1.75, and 2.0 mm according to the manufacturers’ recommendations. The CIELab color space for all specimens placed against a white and black background was measured with a spectrophotometer (CM-2600D), and the translucency parameters were calculated for the materials at various thicknesses. A light-polymerizing unit (DEMI LED) was used to polymerize the resin cement (Variolink II) placed beneath the ceramic specimens. Transmitted light intensity from the polymerization unit beneath the ceramic specimens was measured by using a spectrophotometer (MARC Resin Calibrator), and the transmittance of each specimen was calculated. The coefficient of absorption of each material was calculated from the regression analysis between the natural log of transmittance and specimen thickness. The degree of conversion of resin cement was measured by using a Fourier transformation infrared (FTIR) spectrophotometer. The results were analyzed by using 2-way ANOVA (α=.05). The relationship between the transmittance and the translucency parameter was evaluated by plotting the transmittance against the translucency parameter value of each specimen.
The translucency parameter decreased with increasing thickness in all 5 material groups. All anatomic-contour zirconia had lower translucency parameters than e.max CAD (P<.001). The same results were found for the intensity of the transmitted light (P<.001). Both A2 shade anatomic-contour zirconia (Zirlux and Luxisse) showed significantly lower light transmittance than a generic shade anatomic-contour zirconia (CAP FZ) (P<.001). The coefficients of absorption were found to range from 0.63 to 1.72 mm-1, and reflectance from 0.10 to 0.25. The results from the degree of conversion of resin cement after polymerization through 1 to 2 mm of specimens showed a significantly higher degree of conversion in the e.max group than in all other groups (P<.001). The correlation between translucency parameter and the intensity of the transmitted light suggested that the relationship was shade dependent.
The translucency parameter and the transmitted light intensity of ceramic material were influenced by the type of ceramic and the shade and thickness of the ceramic. The combined effects of layer thickness and the intensity of the transmitted light in the A2 shade anatomic-contour zirconia (Zirlux and Luxisse) resulted in a lower degree of conversion in resin cement than in a generic shade anatomic-contour zirconia (CAP FZ) at layer thicknesses of 1.75 and 2 mm.</abstract><cop>United States</cop><pub>Elsevier Inc</pub><pmid>34116838</pmid><doi>10.1016/j.prosdent.2021.04.019</doi><tpages>7</tpages><oa>free_for_read</oa></addata></record> |
| fulltext | fulltext |
| identifier | ISSN: 0022-3913 |
| ispartof | The Journal of prosthetic dentistry, 2023-01, Vol.129 (1), p.213-219 |
| issn | 0022-3913 1097-6841 |
| language | eng |
| recordid | cdi_proquest_miscellaneous_2540514386 |
| source | MEDLINE; Elsevier ScienceDirect Journals |
| subjects | Ceramics - therapeutic use Color Dental Porcelain Light Materials Testing Resin Cements - therapeutic use Surface Properties |
| title | Effects of shade and thickness on the translucency parameter of anatomic-contour zirconia, transmitted light intensity, and degree of conversion of the resin cement |
| url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-27T12%3A00%3A49IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Effects%20of%20shade%20and%20thickness%20on%20the%20translucency%20parameter%20of%20anatomic-contour%20zirconia,%20transmitted%20light%20intensity,%20and%20degree%20of%20conversion%20of%20the%20resin%20cement&rft.jtitle=The%20Journal%20of%20prosthetic%20dentistry&rft.au=Supornpun,%20Noppamath&rft.date=2023-01&rft.volume=129&rft.issue=1&rft.spage=213&rft.epage=219&rft.pages=213-219&rft.issn=0022-3913&rft.eissn=1097-6841&rft_id=info:doi/10.1016/j.prosdent.2021.04.019&rft_dat=%3Cproquest_cross%3E2540514386%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=2540514386&rft_id=info:pmid/34116838&rft_els_id=S0022391321002511&rfr_iscdi=true |