Influence of Welding Residual Stresses on Fatigue Crack Initiation Life
Fatigue tests were conducted on mild steel (SS41) plate in which residual stresses were varied by different heat treatments: as-welded, and stress relieved at 380, 500 and 620 deg C. Total fatigue life was divided into initiation life and propagation life. The influence of welding tensile residual s...