Observation of crack-closure behavior after single overload cycles in 7075-T6 single-edge-notched specimens
Electrical potential and strain gage techniques were used to determine changes in crack-closure during the delay period after single overload cycles in 7075-T6 SEN specimens. For the specimen geometry (SEN), alloy (7075-T6), and instrumentation used, no significant changes in crack-closure were meas...