Thermomechanical behavior of a polynorbornadiene

A high‐temperature linear amorphous hydrocarbon polymer synthesized cationically from 2,5‐norbornadiene (bicyclo[2.2.1]hepta‐2,5‐diene), was studied thermomechanically with respect to physical transitions and stability in nitrogen. The glass transition temperature was determined to be 320°C (at less...