Depolymerization of cellulose to glucose by oxidation–hydrolysis

An oxidation-hydrolysis strategy was developed for depolymerization of cellulose. Part of the hydroxymethyl groups on glucose units were oxidized to carboxyl groups during the preoxidation treatment, and the generated acid sites act as the catalytic active centers for the following depolymerization of cellulose. After alpha -cellulose was pretreated by air at 210 degree C for 48 h, 23.3% yield of glucose was obtained in water at 150 degree C for 8 h without additional catalyst. The ratio of cellulose/water has no obvious influence on the yield of glucose. 17.9% yield of glucose for alpha -cellulose can still be obtained even at the weight ratio of 0.4, where up to 75 g L super(-1) of glucose solution is obtained. For microcrystalline cellulose, 25.2% yield of glucose was obtained for hydrolysis at 170 degree C for 8 h. It was revealed that the generated carboxyl acid groups in the oxidation step are the catalytic sites for the hydrolysis of cellulose.