Investigate the causes of cracks in welded 310 stainless steel used in the Flare tip

•Microstructural aspects of welding failure causes in the industrial part (Flare tip).•Service condition factors' effects such as temperature and gases, on crack nucleation.•Present a mechanism to prevent the occurrence of cracks in welded stainless steel 310. The present study examines the cau...