Effect of prior laser microstructural refinement on the formation of amorphous layer in an Al86Co7.6Ce6.4 alloy

•Laser microstructural refinement eliminatd large and brittle Al8Co2Ce particles.•Refined microstructure made LAEB homogenisation and amorphisation easier.•Laser microstructural refinement successfully decreased the extent of LAEB cracking. Laser surface melting (LSM) pre-treatment was conducted bef...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Applied surface science 2014-01, Vol.289, p.230-236
Hauptverfasser:	Li, C.L., Murray, J.W., Voisey, K.T., Clare, A.T., McCartney, D.G.
Format:	Artikel
Sprache:	eng
Schlagworte:	Amorphisation Amorphous Brittleness Cracking Crystallisation Electron beam Formations Fracture mechanics Glass formation Glass-forming alloy Homogenisation Homogenizing Laser microstructural refinement Lasers Melting Microstructure Particle size
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!