Effect of specimen pre-cracking method on Delayed Hydride Cracking Rate

Crack propagation rate by the process known as Delayed Hydride Cracking (DHC) is usually assessed in pressure tube materials. Curved Compact Toughness specimens are fatigue pre-cracked previous to DHC test. This work explores the validity of specimen pre-cracking by the same DHC process. It was demo...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of nuclear materials 2012, Vol.420 (1), p.273-277
Hauptverfasser:	Mieza, J.I., De Las Heras, E., Arias, M.I., Domizzi, G.
Format:	Artikel
Sprache:	eng
Schlagworte:	Applied sciences Controled nuclear fusion plants Crack propagation Cracks Energy Energy. Thermal use of fuels Exact sciences and technology Fatigue (materials) Fatigue cracking Fatigue tests Fission nuclear power plants Fracture mechanics Fuels Hydrides Installations for energy generation and conversion: thermal and electrical energy Nuclear fuels Tubes
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!