Intralaminar fatigue crack growth properties of conventional and interlayer toughened CFRP laminate under mode I loading

Intralaminar and interlaminar fatigue crack growth behaviours under mode I loading were investigated with conventional and interlayer toughened unidirectional CFRP laminates. For intralaminar crack growth tests, initial defects were introduced using “intralaminar film insertion method”, in which a release film is inserted inside a single lamina prepreg. A fatigue test under a constant maximum energy release rate, Gmax, was carried out using DCB specimens. It was found that the intralaminar fatigue crack growth property of the interlayer toughened CFRP laminates was the same as that of the conventional CFRP laminates. For the interlayer toughened CFRP laminates, the Gmax with a given crack growth rate, da/dN, was much lower for intralaminar crack growth than for interlaminar crack growth. The da/dN-Gmax curve at zero crack extension, Δa=0, which was estimated by extrapolating the da/dN-Δa relationship, was not affected by bridging fibres, and most conservative for the interlayer toughened CFRP laminates.