Stress Corrosion Cracking of High-strength Drill Pipe in Sour Gas Well
In high sour gas reservoir drilling process, it happens occasionally that high-strength drill pipe suffers brittle fracture failure due to stress corrosion cracking, and poses serious hazard to drilling safety. To solve this problem, this paper studied the stress corrosion cracking mechanism and inf...
Gespeichert in:
| Veröffentlicht in: | Journal of Wuhan University of Technology. Materials science edition 2014-08, Vol.29 (4), p.813-816 |
|---|---|
| Hauptverfasser: | , , , , , , |
| Format: | Artikel |
| Sprache: | eng |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| container_end_page | 816 |
|---|---|
| container_issue | 4 |
| container_start_page | 813 |
| container_title | Journal of Wuhan University of Technology. Materials science edition |
| container_volume | 29 |
| creator | Zhang, Zhi Li, Jing Zeng, Dezhi Hu, Junying Hou, Duo Zhang, Liehui Shi, Taihe |
| description | In high sour gas reservoir drilling process, it happens occasionally that high-strength drill pipe suffers brittle fracture failure due to stress corrosion cracking, and poses serious hazard to drilling safety. To solve this problem, this paper studied the stress corrosion cracking mechanism and infl uencing factors of highstrength drill pipe in sour environment with hydrogen permeation experiments and tensile tests. We simulated practical conditions in laboratory and evaluated the stress corrosion cracking performance of the high-strength drill pipe under conditions of high stress level. For the problems occurring in use of high-strength drill pipe on site, the paper proposed a technical measure for slower stress corrosion cracking. |
| doi_str_mv | 10.1007/s11595-014-1002-8 |
| format | Article |
| fullrecord | <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_miscellaneous_1567107091</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><cqvip_id>662151156</cqvip_id><sourcerecordid>1567107091</sourcerecordid><originalsourceid>FETCH-LOGICAL-c376t-5360bbda2a6d969c0bcb8eb615ec736b7c41077739b2217714c5631c887790df3</originalsourceid><addsrcrecordid>eNp9kDFPwzAQhSMEEqXwA9gsWFgMd3ZixyMKtEVCAqkgxihxndQlTVo7Hfj3uEqFEAOTfdL33r17UXSJcIsA8s4jJiqhgDENM6PpUTRCpTiFmMvj8AcAymLkp9GZ9yuAGLgQo2gy753xnmSdc523XUsyV-hP29akq8jM1kvqA9HW_ZI8ONs05NVuDLEtmXc7R6aFJx-mac6jk6povLk4vOPoffL4ls3o88v0Kbt_pppL0dOECyjLRcEKsVBCaSh1mZpSYGK05KKUOkaQUnJVMoZSYqwTwVGnqZQKFhUfRzeD78Z1253xfb62XocARWu6nc8xETI4gMKAXv9BVyFxG9IFKgEZc4UQKBwoHc73zlT5xtl14b5yhHzfbD40m4dm9zPL06Bhg8YHtq2N--X8j-jqsGjZtfU26H42CcEwCQLBvwE1MIPk</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>1550743910</pqid></control><display><type>article</type><title>Stress Corrosion Cracking of High-strength Drill Pipe in Sour Gas Well</title><source>SpringerLink Journals</source><source>Alma/SFX Local Collection</source><creator>Zhang, Zhi ; Li, Jing ; Zeng, Dezhi ; Hu, Junying ; Hou, Duo ; Zhang, Liehui ; Shi, Taihe</creator><creatorcontrib>Zhang, Zhi ; Li, Jing ; Zeng, Dezhi ; Hu, Junying ; Hou, Duo ; Zhang, Liehui ; Shi, Taihe</creatorcontrib><description>In high sour gas reservoir drilling process, it happens occasionally that high-strength drill pipe suffers brittle fracture failure due to stress corrosion cracking, and poses serious hazard to drilling safety. To solve this problem, this paper studied the stress corrosion cracking mechanism and infl uencing factors of highstrength drill pipe in sour environment with hydrogen permeation experiments and tensile tests. We simulated practical conditions in laboratory and evaluated the stress corrosion cracking performance of the high-strength drill pipe under conditions of high stress level. For the problems occurring in use of high-strength drill pipe on site, the paper proposed a technical measure for slower stress corrosion cracking.</description><identifier>ISSN: 1000-2413</identifier><identifier>EISSN: 1993-0437</identifier><identifier>DOI: 10.1007/s11595-014-1002-8</identifier><language>eng</language><publisher>Heidelberg: Wuhan University of Technology</publisher><subject>Chemistry and Materials Science ; Drill pipe ; Drilling ; Hydrogen permeation ; Materials Science ; Metallic Materials ; Reservoirs ; Simulation ; Sour gas ; Stress corrosion cracking ; Tensile tests ; 含硫气井 ; 应力腐蚀开裂 ; 应力腐蚀裂纹 ; 拉伸试验 ; 钻井过程 ; 钻杆 ; 高含硫气藏 ; 高强度</subject><ispartof>Journal of Wuhan University of Technology. Materials science edition, 2014-08, Vol.29 (4), p.813-816</ispartof><rights>Wuhan University of Technology and Springer-Verlag Berlin Heidelberg 2014</rights><lds50>peer_reviewed</lds50><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c376t-5360bbda2a6d969c0bcb8eb615ec736b7c41077739b2217714c5631c887790df3</citedby></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Uhttp://image.cqvip.com/vip1000/qk/84253X/84253X.jpg</thumbnail><linktopdf>$$Uhttps://link.springer.com/content/pdf/10.1007/s11595-014-1002-8$$EPDF$$P50$$Gspringer$$H</linktopdf><linktohtml>$$Uhttps://link.springer.com/10.1007/s11595-014-1002-8$$EHTML$$P50$$Gspringer$$H</linktohtml><link.rule.ids>314,777,781,27905,27906,41469,42538,51300</link.rule.ids></links><search><creatorcontrib>Zhang, Zhi</creatorcontrib><creatorcontrib>Li, Jing</creatorcontrib><creatorcontrib>Zeng, Dezhi</creatorcontrib><creatorcontrib>Hu, Junying</creatorcontrib><creatorcontrib>Hou, Duo</creatorcontrib><creatorcontrib>Zhang, Liehui</creatorcontrib><creatorcontrib>Shi, Taihe</creatorcontrib><title>Stress Corrosion Cracking of High-strength Drill Pipe in Sour Gas Well</title><title>Journal of Wuhan University of Technology. Materials science edition</title><addtitle>J. Wuhan Univ. Technol.-Mat. Sci. Edit</addtitle><addtitle>Journal of Wuhan University of Technology. Materials Science Edition</addtitle><description>In high sour gas reservoir drilling process, it happens occasionally that high-strength drill pipe suffers brittle fracture failure due to stress corrosion cracking, and poses serious hazard to drilling safety. To solve this problem, this paper studied the stress corrosion cracking mechanism and infl uencing factors of highstrength drill pipe in sour environment with hydrogen permeation experiments and tensile tests. We simulated practical conditions in laboratory and evaluated the stress corrosion cracking performance of the high-strength drill pipe under conditions of high stress level. For the problems occurring in use of high-strength drill pipe on site, the paper proposed a technical measure for slower stress corrosion cracking.</description><subject>Chemistry and Materials Science</subject><subject>Drill pipe</subject><subject>Drilling</subject><subject>Hydrogen permeation</subject><subject>Materials Science</subject><subject>Metallic Materials</subject><subject>Reservoirs</subject><subject>Simulation</subject><subject>Sour gas</subject><subject>Stress corrosion cracking</subject><subject>Tensile tests</subject><subject>含硫气井</subject><subject>应力腐蚀开裂</subject><subject>应力腐蚀裂纹</subject><subject>拉伸试验</subject><subject>钻井过程</subject><subject>钻杆</subject><subject>高含硫气藏</subject><subject>高强度</subject><issn>1000-2413</issn><issn>1993-0437</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2014</creationdate><recordtype>article</recordtype><sourceid>AFKRA</sourceid><sourceid>BENPR</sourceid><sourceid>CCPQU</sourceid><sourceid>DWQXO</sourceid><recordid>eNp9kDFPwzAQhSMEEqXwA9gsWFgMd3ZixyMKtEVCAqkgxihxndQlTVo7Hfj3uEqFEAOTfdL33r17UXSJcIsA8s4jJiqhgDENM6PpUTRCpTiFmMvj8AcAymLkp9GZ9yuAGLgQo2gy753xnmSdc523XUsyV-hP29akq8jM1kvqA9HW_ZI8ONs05NVuDLEtmXc7R6aFJx-mac6jk6povLk4vOPoffL4ls3o88v0Kbt_pppL0dOECyjLRcEKsVBCaSh1mZpSYGK05KKUOkaQUnJVMoZSYqwTwVGnqZQKFhUfRzeD78Z1253xfb62XocARWu6nc8xETI4gMKAXv9BVyFxG9IFKgEZc4UQKBwoHc73zlT5xtl14b5yhHzfbD40m4dm9zPL06Bhg8YHtq2N--X8j-jqsGjZtfU26H42CcEwCQLBvwE1MIPk</recordid><startdate>20140801</startdate><enddate>20140801</enddate><creator>Zhang, Zhi</creator><creator>Li, Jing</creator><creator>Zeng, Dezhi</creator><creator>Hu, Junying</creator><creator>Hou, Duo</creator><creator>Zhang, Liehui</creator><creator>Shi, Taihe</creator><general>Wuhan University of Technology</general><general>Springer Nature B.V</general><scope>2RA</scope><scope>92L</scope><scope>CQIGP</scope><scope>W92</scope><scope>~WA</scope><scope>AAYXX</scope><scope>CITATION</scope><scope>7SR</scope><scope>8AO</scope><scope>8BQ</scope><scope>8FD</scope><scope>8FE</scope><scope>8FG</scope><scope>ABJCF</scope><scope>AFKRA</scope><scope>BENPR</scope><scope>BGLVJ</scope><scope>CCPQU</scope><scope>D1I</scope><scope>DWQXO</scope><scope>HCIFZ</scope><scope>JG9</scope><scope>KB.</scope><scope>PDBOC</scope><scope>PQEST</scope><scope>PQQKQ</scope><scope>PQUKI</scope><scope>PRINS</scope><scope>7SE</scope><scope>FR3</scope><scope>KR7</scope></search><sort><creationdate>20140801</creationdate><title>Stress Corrosion Cracking of High-strength Drill Pipe in Sour Gas Well</title><author>Zhang, Zhi ; Li, Jing ; Zeng, Dezhi ; Hu, Junying ; Hou, Duo ; Zhang, Liehui ; Shi, Taihe</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c376t-5360bbda2a6d969c0bcb8eb615ec736b7c41077739b2217714c5631c887790df3</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng</language><creationdate>2014</creationdate><topic>Chemistry and Materials Science</topic><topic>Drill pipe</topic><topic>Drilling</topic><topic>Hydrogen permeation</topic><topic>Materials Science</topic><topic>Metallic Materials</topic><topic>Reservoirs</topic><topic>Simulation</topic><topic>Sour gas</topic><topic>Stress corrosion cracking</topic><topic>Tensile tests</topic><topic>含硫气井</topic><topic>应力腐蚀开裂</topic><topic>应力腐蚀裂纹</topic><topic>拉伸试验</topic><topic>钻井过程</topic><topic>钻杆</topic><topic>高含硫气藏</topic><topic>高强度</topic><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>Zhang, Zhi</creatorcontrib><creatorcontrib>Li, Jing</creatorcontrib><creatorcontrib>Zeng, Dezhi</creatorcontrib><creatorcontrib>Hu, Junying</creatorcontrib><creatorcontrib>Hou, Duo</creatorcontrib><creatorcontrib>Zhang, Liehui</creatorcontrib><creatorcontrib>Shi, Taihe</creatorcontrib><collection>中文科技期刊数据库</collection><collection>中文科技期刊数据库-CALIS站点</collection><collection>中文科技期刊数据库-7.0平台</collection><collection>中文科技期刊数据库-工程技术</collection><collection>中文科技期刊数据库- 镜像站点</collection><collection>CrossRef</collection><collection>Engineered Materials Abstracts</collection><collection>ProQuest Pharma Collection</collection><collection>METADEX</collection><collection>Technology Research Database</collection><collection>ProQuest SciTech Collection</collection><collection>ProQuest Technology Collection</collection><collection>Materials Science & Engineering Collection</collection><collection>ProQuest Central UK/Ireland</collection><collection>ProQuest Central</collection><collection>Technology Collection</collection><collection>ProQuest One Community College</collection><collection>ProQuest Materials Science Collection</collection><collection>ProQuest Central Korea</collection><collection>SciTech Premium Collection</collection><collection>Materials Research Database</collection><collection>Materials Science Database</collection><collection>Materials Science Collection</collection><collection>ProQuest One Academic Eastern Edition (DO NOT USE)</collection><collection>ProQuest One Academic</collection><collection>ProQuest One Academic UKI Edition</collection><collection>ProQuest Central China</collection><collection>Corrosion Abstracts</collection><collection>Engineering Research Database</collection><collection>Civil Engineering Abstracts</collection><jtitle>Journal of Wuhan University of Technology. Materials science edition</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Zhang, Zhi</au><au>Li, Jing</au><au>Zeng, Dezhi</au><au>Hu, Junying</au><au>Hou, Duo</au><au>Zhang, Liehui</au><au>Shi, Taihe</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Stress Corrosion Cracking of High-strength Drill Pipe in Sour Gas Well</atitle><jtitle>Journal of Wuhan University of Technology. Materials science edition</jtitle><stitle>J. Wuhan Univ. Technol.-Mat. Sci. Edit</stitle><addtitle>Journal of Wuhan University of Technology. Materials Science Edition</addtitle><date>2014-08-01</date><risdate>2014</risdate><volume>29</volume><issue>4</issue><spage>813</spage><epage>816</epage><pages>813-816</pages><issn>1000-2413</issn><eissn>1993-0437</eissn><abstract>In high sour gas reservoir drilling process, it happens occasionally that high-strength drill pipe suffers brittle fracture failure due to stress corrosion cracking, and poses serious hazard to drilling safety. To solve this problem, this paper studied the stress corrosion cracking mechanism and infl uencing factors of highstrength drill pipe in sour environment with hydrogen permeation experiments and tensile tests. We simulated practical conditions in laboratory and evaluated the stress corrosion cracking performance of the high-strength drill pipe under conditions of high stress level. For the problems occurring in use of high-strength drill pipe on site, the paper proposed a technical measure for slower stress corrosion cracking.</abstract><cop>Heidelberg</cop><pub>Wuhan University of Technology</pub><doi>10.1007/s11595-014-1002-8</doi><tpages>4</tpages></addata></record> |
| fulltext | fulltext |
| identifier | ISSN: 1000-2413 |
| ispartof | Journal of Wuhan University of Technology. Materials science edition, 2014-08, Vol.29 (4), p.813-816 |
| issn | 1000-2413 1993-0437 |
| language | eng |
| recordid | cdi_proquest_miscellaneous_1567107091 |
| source | SpringerLink Journals; Alma/SFX Local Collection |
| subjects | Chemistry and Materials Science Drill pipe Drilling Hydrogen permeation Materials Science Metallic Materials Reservoirs Simulation Sour gas Stress corrosion cracking Tensile tests 含硫气井 应力腐蚀开裂 应力腐蚀裂纹 拉伸试验 钻井过程 钻杆 高含硫气藏 高强度 |
| title | Stress Corrosion Cracking of High-strength Drill Pipe in Sour Gas Well |
| url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-18T07%3A59%3A11IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Stress%20Corrosion%20Cracking%20of%20High-strength%20Drill%20Pipe%20in%20Sour%20Gas%20Well&rft.jtitle=Journal%20of%20Wuhan%20University%20of%20Technology.%20Materials%20science%20edition&rft.au=Zhang,%20Zhi&rft.date=2014-08-01&rft.volume=29&rft.issue=4&rft.spage=813&rft.epage=816&rft.pages=813-816&rft.issn=1000-2413&rft.eissn=1993-0437&rft_id=info:doi/10.1007/s11595-014-1002-8&rft_dat=%3Cproquest_cross%3E1567107091%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=1550743910&rft_id=info:pmid/&rft_cqvip_id=662151156&rfr_iscdi=true |