Mechanics of fatigue crack growth in a bonding interface

Experimental investigations have shown that cracks in a bonding interface such as adhesives or brazings under cyclic loading behave fundamentally different from cracks in homogeneous metals. In particular the slope of da/dN-vs.-IK-curves is much steeper and the threshold value higher than in homogen...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Engineering fracture mechanics 2012-07, Vol.89, p.52-64
Hauptverfasser:	Schindler, Hans-Jakob, Leinenbach, Christian
Format:	Artikel
Sprache:	eng
Schlagworte:	Crack opening displacement Crack propagation Fatigue failure Fracture mechanics Mathematical analysis Plastic zones Shielding Thresholds