Research on size effects in the low‐velocity impact (LVI) and compression after impact (CAI) characteristics of composite laminates

The load‐bearing capacity and failure characteristics of composite structures are closely related to their dimensions. In this study, low‐velocity impact, ultrasonic non‐destructive testing, and compression after impact tests were conducted on composite laminates of varying widths to investigate the...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Polymer composites 2024-09, Vol.45 (13), p.12405-12420
Hauptverfasser:	Zou, Xionghui, Gao, Weicheng, Xi, Wei
Format:	Artikel
Sprache:	eng
Schlagworte:	Bearing capacity Composite structures compression after impact Compression loads Compression tests Compressive strength Damage assessment Damage localization Delamination Destructive testing Energy absorption Equivalence failure Failure modes Impact loads Impact response Impact tests Laminates Load low‐velocity impact Peak load Residual energy Residual strength Size effects ultrasonic C‐scan Ultrasonic testing widths
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!