Comparison of damage mechanisms in chopped strand mat and woven roving mat composites under cyclic tension

Glass fiber reinforced polymer (GFRP) composites with chopped strand mat (CSM) and woven roving mat (WRM) reinforcements are widely used in high‐pressure piping due to their favorable strength‐to‐weight ratio. However, cyclic loading from vibrations and pulsating forces can induce internal microstru...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Polymer composites 2024-08, Vol.45 (12), p.11162-11177
Hauptverfasser:	Hiremath, Mritunjay M., Bernthaler, Timo, Anger, Pascal, Mishra, Sushil K., Guha, Anirban, Tewari, Asim
Format:	Artikel
Sprache:	eng
Schlagworte:	Chopped strand mats Crack initiation Cracks Cyclic loads damage mechanics Damage patterns electron microscopy fatigue Fatigue cracks Fatigue failure Fiber composites Fiber orientation Fiber reinforced polymers Finite element method Fracture mechanics Glass fiber reinforced plastics glass fibers Matrix cracks Microcracks Performance degradation Shear stress Three dimensional composites