$Effect of surface roughness and polishing orientation on fatigue life and fracture fatigue entropy$

Effect of surface roughness and polishing orientation on fatigue life and fracture fatigue entropy

The effect of surface roughness and polishing orientation on fatigue life is investigated. Fully reversed bending fatigue tests are conducted on ASTM A1008 specimens having surface roughness asperities ranging from mirror finish (Ra = 0.05 μm) to coarse (Ra = 1.5 μm). Two polishing directions (i.e.,...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Fatigue & fracture of engineering materials & structures 2024-05, Vol.47 (5), p.1514-1530
Hauptverfasser:	Hebert, John, Khonsari, M. M.
Format:	Artikel
Sprache:	eng
Schlagworte:	Asperity Bend tests Bending fatigue Entropy Fatigue failure Fatigue life Fatigue tests fracture fatigue entropy (FFE) Orientation Polishing remaining useful life Reversed bending surface finish Surface roughness Surface roughness effects surface roughness orientation
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!