Degradation Pathways of Cobalt‐Free LiNiO2 Cathode in Lithium Batteries

Electrode‐electrolyte reactivity (EER) and particle cracking (PC) are considered two main causes of capacity fade in high‐nickel layered oxide cathodes in lithium‐based batteries. However, whether EER or PC is more critical remains debatable. Herein, the fundamental correlation between EER and PC is...