Element-resolved electrochemical analysis of the passivity of additively manufactured stainless steel 316L
•The ‘true’ corrosion rate of AM-316L was lower than that of the W-316L in 0.6 M NaCl.•The fraction of Cr2O3 was relatively higher in the passive film of AM-316L than that of the W-316L.•The Mn(Si, Al) rich oxide nano-particles present in AM-316L dissolved preferentially in 0.6 M NaCl.•Surface compo...