Corrosion fatigue life prediction of crude oil storage tank via improved equivalent initial flaw size

•EIFS is improved for corrosion fatigue life prediction.•Corrosion fatigue life prediction model is developed via I-EIFS.•Corrosion fatigue life of COST is predicted with proposed model.•The validity of life prediction method for COST is verified by comparing service life. Corrosion fatigue is ident...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Theoretical and applied fracture mechanics 2021-08, Vol.114, p.103023, Article 103023
Hauptverfasser:	Zhang, Yuru, Liu, Xintian, Lai, Jiafeng, Wei, Yuwei, Luo, Jiao
Format:	Artikel
Sprache:	eng
Schlagworte:	Bending fatigue Corrosion Corrosion fatigue Corrosion mechanisms Corrosion tests COST Crack propagation Crude oil EIFS Equivalence Failure analysis Failure mechanisms Fatigue cracks Fatigue failure Fatigue life I-EIFS Life prediction Pitting (corrosion) Service life Storage tanks Stress corrosion cracking
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!