Effect of aging on structure and strength of high pressure torsion processed 2024 aluminum alloy

Pre-quenched samples with a diameter of 20 mm and a thickness of 1 mm, cut from commercial hot-pressed rod of the 2024 aluminum alloy, were severely deformed by high-pressure torsion (HPT) with 10 revolutions under a pressure of 6 GPa at room temperature and then annealed for up to 50 hours in the t...