Corrosion fatigue behaviour of HFMI-treated butt welds

•Investigating influence of corrosion on the efficiency of HFMI.•Application of laboratory tests to simulate real marine corrosion conditions.•Correlation between laboratory and real conditions based on a previous study.•Influence of loading mode taken into consideration.•Boundaries of the research...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of fatigue 2021-04, Vol.145, p.106079, Article 106079
Hauptverfasser:	Gkatzogiannis, Stefanos, Weinert, Joscha, Engelhardt, Imke, Knoedel, Peter, Ummenhofer, Thomas
Format:	Artikel
Sprache:	eng
Schlagworte:	Artificial seawater Bending fatigue Corrosion fatigue Corrosion resistance Crack initiation Crack propagation Fatigue failure Fatigue life Fatigue strength Fatigue tests Fracture mechanics High frequency mechanical impact Laboratories Marine corrosion Material removal rate (machining) Materials fatigue Reduction Research projects S355J2+N Salt spray chamber test Seawater Structural steels Surface layers Surface roughness Tempering
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!