Hot deformation behavior and flow stress modeling of Ti–6Al–4V alloy produced via electron beam melting additive manufacturing technology in single β-phase field

The hot working behaviour of additively manufactured Ti–6Al–4V pre-forms by Electron Beam Melting (EBM) has been studied at temperatures of 1000–1200 °C and strain rates of 0.001–1 s−1. As a reference, a wrought Ti–6Al–4V alloy was also analyzed as same as the EBM one. In order to investigate the ho...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Materials science & engineering. A, Structural materials : properties, microstructure and processing Structural materials : properties, microstructure and processing, 2020-08, Vol.792, p.139822, Article 139822
Hauptverfasser: Saboori, Abdollah, Abdi, Ata, Fatemi, Seyed Ali, Marchese, Giulio, Biamino, Sara, Mirzadeh, Hamed
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The hot working behaviour of additively manufactured Ti–6Al–4V pre-forms by Electron Beam Melting (EBM) has been studied at temperatures of 1000–1200 °C and strain rates of 0.001–1 s−1. As a reference, a wrought Ti–6Al–4V alloy was also analyzed as same as the EBM one. In order to investigate the hot working behaviour of these samples, all the data evaluations were carried out step by step, and the stepwise procedure was discussed. No localized strain as a consequence of shear band formation was found in the samples after the hot compression. The flow stress curves of all the samples showed peak stress at low strains, followed by a regime of flow softening with a near-steady-state flow at large strains. Interestingly, it is found that the initial microstructure and porosity content as well as the chemistry of material (e.g. oxygen content) as being possible contributors to the lower level of flow stress that could be beneficial from the industrial point of view. The flow softening mechanism(s) were discussed in detail using the microstructure of the specimens before and after the hot deformation. Dynamic Recrystalization (DRX) could also explain the gentle oscillation in the appearance of the flow softening curves of the EBM samples. Moreover, the hot working analysis indicated that the activation energy for hot deformation of as-built EBM Ti–6Al–4V alloy was calculated as ~193.25 kJ/mol, which was much lower than the wrought alloy (229.34 kJ/mol). These findings can shed lights on a new integration of metal Additive Manufacturing (AM) and thermomechanical processing. It is very interesting to highlight that through this new integration, it would be possible to reduce the forging steps and save more energy and materials with respect to the conventional routes. •Hot working behaviour of as-built EBM is carried out for the first time.•EBM can be employed to fabricate Ti–6Al–4V pre-forms for hot forming.•This new integration of AM with conventional processes can reduce the number of forging passes.•No localized stain as a result of shear band formation is found.•EBM specimens have lower flow stress and higher grade of DRX.
ISSN:0921-5093
1873-4936
DOI:10.1016/j.msea.2020.139822