Research on Fatigue Life Prediction and Reliability of High Strength and Toughness Aluminum Alloys

According to the fatigue test statistical analysis method, the median S – N curve and the p - S – N curve with 99.9% survival rate of smooth specimens of high strength and toughness Al–Zn–Mg–Cu alloy are obtained. Based on these curves, the reliability analysis of test data under different stress am...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of failure analysis and prevention 2020-08, Vol.20 (4), p.1399-1407
Hauptverfasser:	Jian, Haigen, Yang, Xiaomei, Wang, Yedong, Lei, Xinlei, Zhang, Wei, Mi, Chengji
Format:	Artikel
Sprache:	eng
Schlagworte:	Alloys Aluminum base alloys Characterization and Evaluation of Materials Chemistry and Materials Science Classical Mechanics Copper Corrosion and Coatings Crack propagation Fatigue failure Fatigue life Fatigue tests Fracture mechanics High strength alloys Life prediction Magnesium Materials Science Metal fatigue Quality Control Reliability Reliability analysis Safety and Risk Service life Solid Mechanics Statistical analysis Stress intensity factors Technical Article > -Peer-Reviewed Tribology Zinc
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!