Mechanical degradation of Fe-C-X steels by acidic stress-corrosion cracking

•In-situ tensile testing of Fe-C-X steels in acidic environment to assess SCC•Stress-corrosion cracks and reduced ductility and strength observed in acidic water•Anodic dissolution and hydrogen embrittlement contributed to mechanical degradation•Linear correlation between amount SCC embrittlement an...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Corrosion science 2020-05, Vol.167, p.108509, Article 108509
Hauptverfasser:	De Seranno, Tim, Vandewalle, Liese, Depover, Tom, Verliefde, Arne R.D., Verbeken, Kim
Format:	Artikel
Sprache:	eng
Schlagworte:	A. Acid solutions A. Low alloy steel Anodic dissolution Aqueous environments B. SEM C. Anodic dissolution C. Hydrogen embrittlement C. Stress corrosion Chromium Corrosion Cracks Degradation Dissolution Hydrogen embrittlement Iron Molybdenum Quenching Stress corrosion cracking
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!