A Comparative Study of Residual Stress Distribution Induced by Hard Machining Versus Grinding

This study investigates the residual stress distribution induced by hard machining and grinding and compares its impact on fatigue parameters. The residual stress distribution below hard turned and ground surfaces is investigated after a thermally damaged layer is removed. Fatigue parameters are com...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Tribology letters 2009-12, Vol.36 (3), p.277-284
1. Verfasser:	Choi, Youngsik
Format:	Artikel
Sprache:	eng
Schlagworte:	Chemistry and Materials Science Comparative studies Contact stresses Corrosion and Coatings Crack initiation Crack propagation Fatigue failure Fatigue life Fatigue tests Fracture mechanics Grinding Life prediction Machining Materials Science Nanotechnology Original Paper Parameters Physical Chemistry Residual stress Rolling contact Shear stress Stress concentration Stress distribution Surfaces and Interfaces Theoretical and Applied Mechanics Thin Films Tribology Ultrasonic testing
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!