Orientation dependent fatigue performance and mechanisms of selective laser melted maraging steel X3NiCoMoTi18-9-5

Additive manufacturing (AM) of the maraging steel X3NiCoMoTi18-9-5 (or 18Ni300) is readily used for close contour cooling of complex forming dies or injection moulding dies, and can be used at long-term operating temperatures up to 400 °C. Therefore, this study aims to establish an understanding of...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of fatigue 2019-10, Vol.127, p.395-402
Hauptverfasser:	Damon, James, Hanemann, Theresa, Dietrich, Stefan, Graf, Gregor, Lang, Karl-Heinz, Schulze, Volker
Format:	Artikel
Sprache:	eng
Schlagworte:	Anisotropy Build orientation fatigue Crack initiation Crack propagation Defects Dependence Die forming Fatigue failure Fatigue strength Forming dies Fracture mechanics Fracture surfaces High cycle fatigue Inclusions Injection molding Laser beam melting Maraging steel Maraging steels Materials fatigue Mechanical tests Microstructure Operating temperature Orientation Porosity Process inherent defects Selective laser melting
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!