Damage Process and Measurement of Crystal Misorientation by EBSD under Creep and Creep Fatigue Conditions on Ni Base Alloy HR6WNi基合金

Nickel based alloy HR6W is one of candidate materials for high-temperature components in an advanced ultra-super critical power plant in Japan. In application to piping, it is necessary to clarify progress of damage and life property under creep and creep-fatigue loading conditions. In this study, f...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Zairyō 2019-01, Vol.68 (8), p.614
Hauptverfasser:	MIYAMOTO, Kenta, OGATA, Takashi
Format:	Artikel
Sprache:	jpn
Schlagworte:	Crack propagation Creep fatigue Damage accumulation Ductility tests Electric power generation Electron backscatter diffraction Exhaustion Fatigue Fatigue cracks Fatigue failure Fatigue life Fatigue tests Fracture mechanics High temperature Materials selection Misalignment Nickel base alloys Piping Property damage
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!