On the stability of PEEK for short processing cycles at high temperatures and oxygen-containing atmosphere

The motivation of this study was to investigate the stability of poly(ether ether ketone) (PEEK) at conditions close to real processing: fast cycles (below 300 s), temperatures higher than 400 °C and oxygen-containing atmosphere. Such conditions significantly affect the consolidation ability of PEEK...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Polymer degradation and stability 2019-07, Vol.165, p.161-169
Hauptverfasser:	Pascual, Alfons, Toma, Michael, Tsotra, Panayota, Grob, Markus C.
Format:	Artikel
Sprache:	eng
Schlagworte:	Barrier layers Boundary layer Boundary layers Change detection Consolidation Crosslinking Degradation Differential scanning calorimetry Diffusion layers Fourier transforms High temperature Infrared radiation IR-Microscopy Light transmission Oxygen poly(ether ether ketone) Polyether ether ketones Polymers Semi-finished products Stability Thermo-oxidative degradation Thermogravimetric analysis
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!