Kinetics of carbon steel dissolution in ammonium chloride solution containing sodium thiosulfate

The dissolution behavior of carbon steel in ammonium chloride (NH4Cl) solution containing sodium thiosulfate (Na2S2O3) of various concentrations (0.01 and 0.1 M) was investigated using electrochemical impedance spectroscopy (EIS) and other nonelectrochemical techniques. The weight loss and polarization measurements indicate a significant increase in the NH4Cl corrosion rate of carbon steel on addition of Na2S2O3. The EIS measurements exhibited two capacitive loops at multiple direct current (dc) potentials for both the concentrations. Electrical equivalent circuit (EEC) and reaction mechanism analysis (RMA) were employed to analyze the impedance data. A four‐step mechanism with two intermediate adsorbate species of same charge was proposed to explain the dissolution behavior of carbon steel in the given system. The surface coverage values enumerated that the surface was entirely covered with adsorbed species unlike in the pure NH4Cl system. Charge transfer resistance and polarization resistance values estimated from RMA parameters indicate the increase in a dissolution rate with dc potential. The surface morphology was inspected via field emission scanning electron microscopy, and the corrosion products including surface state of carbon steel electrode were analyzed using energy dispersive X‐ray spectroscopy and X‐ray photoelectron spectroscopy.