The durability of the thermally decomposed IrO2-Ta2O5 coated titanium anode in a sulfate solution
•The deactivation was due to coating loss or combined with passivation of the titanium substrate.•The coating loss was occurring as coating dissolution, coating spalling and coating peeling off.•No critical value of the amount of the residual iridium was found in this work to predict the eventual de...