An efficient phase-field model for fatigue fracture in ductile materials

Fatigue fracture in ductile materials, e. g. metals, is caused by cyclic plasticity. Especially regarding the high numbers of load cycles, plastic material models resolving the full loading path are computationally very demanding. Herein, a model with particularly small computational effort is prese...