Analysis of the single overload effect on fatigue crack growth in AA 2024-T3 plates repaired with composite patch

[Display omitted] •The fatigue crack leads to retardation followed by overload or bonded patch repair with different consequences.•If the patch is bonded before the overload, the two effects nullify partially and the effect the overall fatigue life of the structure.•If the patch is bonded after the...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Engineering fracture mechanics 2018-10, Vol.202, p.147-161
Hauptverfasser:	Mohammed, Sohail M. A. Khan, Bouiadjra, B. Bachir, Benyahia, F., Albedah, A.
Format:	Artikel
Sprache:	eng
Schlagworte:	Aluminum Aluminum alloy Aluminum base alloys Bonded composite repair Crack propagation Cracks Fatigue crack growth Fatigue failure Fatigue life Fatigue tests Fractography Fracture mechanics Life extension Load history Materials fatigue Overload Patching Repair
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!