A new mixed mode I/II failure criterion for laminated composites considering fracture process zone

•A mixed mode I/II failure criterion was proposed for prediction of the crack growth in orthotropic materials.•The newly proposed criterion considers the absorbed energy in the fracture process zone by defining a suitable damage factor.•The applicability of the new criterion was investigated in both...