The effect of the solidification rate on the physical properties of the Sn-Zn eutectic alloy

As-cast Sn-8.8 wt.% Zn eutectic alloy was directionally solidified with a constant temperature gradient (G = 4.16 K/mm) under various solidification rates (V = 8.3–790 μm/s) in a Bridgman-type furnace. The dependence of the microhardness (HV), ultimate tensile strength (σut), ultimate compressive st...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Physica. B, Condensed matter Condensed matter, 2018-09, Vol.545, p.48-54
Hauptverfasser:	Şahin, Mevlüt, Karakurt, Fatih
Format:	Artikel
Sprache:	eng
Schlagworte:	Alloys Compressive strength Directional solidification Electrical resistivity Enthalpy Eutectic alloys Heat conductivity Mathematical analysis Microhardness Physical properties Resistivity Temperature dependence Temperature gradients Tensile strength Thermal conductivity Ultimate tensile strength
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!