Effect of Zn addition on bulk microstructure of lead-free solder SN100C

This paper reports the effect of adding Zn (0.5 wt% Zn, 1.0 wt% Zn) to the bulk microstructure and intermetallic compound (IMC) formation of commercial SN100C (Sn-0.7Cu-0.05Ni+Ge) lead-free solder alloy. Solder alloys were prepared by melting SN100C ingot and Zn shots, and subsequently casted into steel mold. Samples were ground and polished for XRF, and polished samples were then etched for microstructure analysis. Microstructure of bulk solder and the IMC were observed using SEM equipped with EDX. SEM result showed the addition of 0.5 wt% Zn resulted in increased grain size of β-Sn matrix but further addition of Zn (1 wt%) reduced the size of β-Sn dendrites in the bulk solder. Several intermetallic compounds (IMCs) were observed distributed in the Sn matrix; Cu-Zn, Ni-Zn and Cu-Zn-Ni IMC but in relatively small percentage compared to Cu-Zn and Ni-Zn. These particles could be considered as effective nucleating agent that led to finer β-Sn grains. It is expected that the finer β-Sn will contribute towards higher solder strength and the various IMCs present could act as suppressant for Sn diffusion which will then tend to reduce the IMC growth during thermal aging.