Failure Analysis of an Automotive Bushing

The cause of a longitudinal fracture of an automotive bushing during the assembly process is presented in this study. On the basis of macroscopic inspection, scanning electron microscopy, energy-dispersive spectroscopy, microstructural examination, chemical analysis and hardness measurements, cleava...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of failure analysis and prevention 2018-12, Vol.18 (6), p.1379-1385
Hauptverfasser:	Deng, Ailin, Xue, Song, Guo, Ruidong
Format:	Artikel
Sprache:	eng
Schlagworte:	Assembly Characterization and Evaluation of Materials Chemical analysis Chemistry and Materials Science Classical Mechanics Corrosion and Coatings Crack propagation Decarburization Decarburizing Failure analysis Fracture surfaces Inspection Materials Science Metallurgical analysis Organic chemistry Quality Control Reliability Safety and Risk Scanning electron microscopy Solid Mechanics Stress concentration Stress propagation Surface defects Technical Article > -Peer-Reviewed Tribology
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!