Corrosion experiments on IN-RAFM steel in flowing lead-lithium for Indian LLCB TBM

•Corrosion rate of IN-RAFMS with Pb-16Li, at ∼465° C and flowing at ∼10 cm/s velocity is ∼44 μm/year.•Iron and chromium were found leaching from near surface regions.•Reduction in hardness observed up to 40 μm, after exposure for 5000 h.•Mechanical properties of the steel were not much affected, aft...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Fusion engineering and design 2018-07, Vol.132, p.52-59
Hauptverfasser:	Atchutuni, Sarada Sree, Saraswat, Abhishek, Sasmal, Chandra Sekhar, Verma, S., Prajapati, Ashok K., Jaiswal, Ankur, Gupta, Sandeep, Chauhan, Jignesh, Pandya, Karishma B., Makwana, Mayank, Tailor, Hardik, Agravat, Hemang S., P., Prasad Rao, E., Rajendra Kumar
Format:	Artikel
Sprache:	eng
Schlagworte:	Chromium Corrosion Corrosion rate Elongation Eutectics Exposure Ferritic stainless steels IN-RAFM steel Leaching Lead Lithium LLCB TBM Martensitic stainless steels Metallurgy Micro vicker’s hardness Pb-Li Pump driven loop Reduction Tensile strength Weight loss measurement
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!