dK/da effects on the SCC growth rates of nickel base alloys in high-temperature water

The effect of dK/da on crack growth behavior of nickel base alloys has been studied by conducting stress corrosion cracking tests under positive and negative dK/da loading conditions on Alloys 690, 600 and X-750 in high temperature water. Results indicate that positive dK/da accelerates the SCC grow...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of nuclear materials 2018-05, Vol.503, p.13-21
Hauptverfasser:	Chen, Kai, Wang, Jiamei, Du, Donghai, Andresen, Peter L., Zhang, Lefu
Format:	Artikel
Sprache:	eng
Schlagworte:	Alloys Corrosion tests Crack growth rate Crack propagation dK/da Growth rate High temperature High temperature water Nickel Nickel alloys Nickel base alloys Nuclear chemistry Strain hardening Strain rate Stress corrosion Stress corrosion cracking Water temperature
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!