Fatigue and crack-growth behavior in a titanium alloy under constant-amplitude and spectrum loading

•Fatigue tests conducted on titanium alloy (STOA) material from previous U.S. Air Force study.•Fatigue specimen was a newly-developed single-edge-notch-bend specimen.•Fatigue tests conducted under constant-amplitude and spectrum (Cold-Turbistan) loading.•Fatigue-crack-growth data on compact specimen...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Engineering fracture mechanics 2018-01, Vol.187, p.211-224
Hauptverfasser:	Newman, J.C., Kota, K., Lacy, T.E.
Format:	Artikel
Sprache:	eng
Schlagworte:	Amplitudes Compression tests Crack closure Crack propagation Cracks Cumulative damage Fatigue Fatigue cracking Fatigue failure Fatigue life Fatigue tests Fracture mechanics High cycle fatigue Materials fatigue Plasticity Plate material Precracking Predictions Spectrum loading Stress-intensity factor Titanium alloys Titanium base alloys
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!