$Interlaminar fracture toughness of 5HS Carbon/PEEK laminates. A comparison between DCB, ELS and mandrel peel tests$

Interlaminar fracture toughness of 5HS Carbon/PEEK laminates. A comparison between DCB, ELS and mandrel peel tests

The present work focuses on the applicability of the mandrel peel test to quantify the interlaminar fracture toughness of 5 harness satin woven fabric Carbon/PEEK composites. For this purpose, the Mandrel Peel (MP) test was compared to the Double Cantilever Beam (DCB) and End-Loaded Split (ELS) test...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Polymer testing 2018-04, Vol.66, p.13-23
Hauptverfasser:	Sacchetti, Francisco, Grouve, Wouter J.B., Warnet, Laurent L., Fernandez Villegas, Irene
Format:	Artikel
Sprache:	eng
Schlagworte:	Cantilever beams Carbon fiber reinforced plastics Crack initiation Crack propagation Fracture mechanics Fracture toughness Laminates Peel tests Polymer matrix composites Propagation Stability Thermoplastic composites Thermoplastics