Study on shot peened residual stress distribution under cyclic loading by numerical analysis

To prevent stress corrosion cracking or to extend the fatigue life of structures, various peening techniques are employed. In this research, to reproduce the residual stress distribution after shot peening, the residual stress due to multi-pass welding was predicted and the analysis of shot peening...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Yōsetsu Gakkai ronbunshū 2017-01, Vol.35 (2), p.75s
Hauptverfasser:	Ikushima, Kazuki, Kitani, Yuji, Shibahara, Masakazu, Nishikawa, Satoru, Furukawa, Takashi, Akita, Koichi, Suzuki, Hiroshi, Morooka, Satoshi
Format:	Artikel
Sprache:	eng ; jpn
Schlagworte:	Compressive properties Corrosion fatigue Crack propagation Cyclic loads Fatigue cracking Fatigue failure Fatigue life Finite element method Fracture mechanics Load distribution (forces) Nonlinear analysis Numerical analysis Residual stress Shot peening Stress concentration Stress corrosion cracking Stress distribution Welding
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!