Hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 °C

The hot corrosion of Ni, Cr, and 80Ni20Cr in the presence of NaCl and water vapor at 750 °C was studied. The results indicated that no significant oxidation or corrosion effect of Ni was found in this case. However, a severe damage caused by the synergistic effect of NaCl deposit and water vapor on...