Effects of macro-scale corrosion damage feature on fatigue crack initiation and fatigue behavior

•Presence of corrosion damage greatly reduced the total fatigue life of AA7050-T7451.•The fatigue crack initiation life for different corrosion morphologies is relatively constant.•The macro-scale metrics analyzed do not fully dictate the location of fatigue crack formation site.•Crack growth rates...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of fatigue 2017-10, Vol.103, p.234-247
Hauptverfasser:	Co, Noelle Easter C., Burns, James T.
Format:	Artikel
Sprache:	eng
Schlagworte:	Aluminum Aluminum base alloys Computed tomography Corrosion Corrosion effects Corrosion fatigue Corrosion morphology Corrosion rate Crack initiation Crack propagation Electrochemical potential Fatigue crack growth Fatigue failure Fatigue initiation Fatigue life Fracture mechanics Materials fatigue Mathematical morphology Morphology Pits Recession Stress corrosion cracking Uniform attack (corrosion) White light
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!