Long term creep-fatigue interaction studies on India-specific reduced activation ferritic-martensitic (IN-RAFM) steel

Deterioration in fatigue life occurs due to introduction of hold in peak tensile or peak compressive or in both peak tensile and compressive strains in a triangular waveform. The hold period of a creep fatigue interaction (CFI) cycle denote the uninterrupted service period during which creep damage...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of fatigue 2017-05, Vol.98, p.259-268
Hauptverfasser:	Shankar, Vani, Mariappan, K., Sandhya, R., Laha, K., Bhaduri, A.K.
Format:	Artikel
Sprache:	eng
Schlagworte:	Activation Activation analysis Cold flow Compressive properties Crack propagation Creep fatigue Creep fatigue interaction Damage assessment Deterioration Fatigue failure Fatigue life Fatigue tests Ferritic stainless steels Low cycle fatigue Martensitic stainless steels Materials creep Materials fatigue Oxidation Plastic deformation Plastic strain RAFM steel Stress relaxation Tensile strength Waveform analysis
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!