Control of Impact-Abrasion Resistance by Changing the Austenitising Temperature of 25 % Cr Cast Irons
The austenitising temperature for 3 mass % C-25 mass % Cr cast iron was changed from 1120 K up to 1470 K to change the hardness as well as the amount of retained austenite after air hardening, and the relation to weight loss resulting from impact wear was investigated. To evaluate weight loss due to...